Observation of phase transition of thermo-responsive poly(NIPA)-PEI block copolymers by STM

Academic Press Inc Elsevier Science
Publication Type:
Journal Article
Journal of Colloid and Interface Science, 2002, 251 (2), pp. 424 - 428
Issue Date:
Full metadata record
Files in This Item:
Filename Description SizeFormat
2006008425.pdf162 kBAdobe PDF
N-isopropylacrylamide (NIPA) homopolymers having carboxylic acid-end groups were synthesized by using mercaptoacetic acid (MAA) as the chain transfer agent. Polymerization was achieved in ethanol using azobisisobutyronitrile (AIBN) as the initiator. Average molecular weight of the homopolymer estimated by titration was 1958. This carboxylic acid-ended poly(NIPA) was then copolymerized with polyethylenimine (PEI, MW-2000) using a water soluble carbodiimide (EDAC). With respect to carboxyl-ended poly(NIPA), the block copolymers exhibited a pH dependent-temperature sensitivity and higher LCST values in acidic pH. Scanning tunneling microscopy (STM) images of both the homopolymer and the copolymer were obtained at 25 and 45°C with tip-sample bias voltages of up to 800 mV and tunneling currents not, vert, similar1 nA. These images showed that STM can be used to visualize both the formation of copolymer chains and their structure, and also their stimuli-responsive behavior.
Please use this identifier to cite or link to this item: