Effect Of Coiling Temperature On Oxide Scale Of Hot-rolled Strip

Publisher:
Trans Tech Publications Ltd
Publication Type:
Conference Proceeding
Citation:
Advanced Materials, Pts 1-3, 2012, pp. 853 - 858
Issue Date:
2012-01
Full metadata record
Files in This Item:
Filename Description Size
Thumbnail2013003156OK.pdf Published version1.09 MB
Adobe PDF
The influence of the coiling temperature, ranging from 550 to 570 degrees C, on the morphology and the phase composition of the oxide scale formed on the microalloyed low carbon steel for automobiles after hot strip rolling was investigated. Physicochemical characteristics of the oxide scales were examined and their formation mechanism was discussed. Thickness of the oxide scale is in the range of 8-11 mu m and decreases with a decrease of coiling temperature. The microstructure and phase composition, XRD analysis shows a large amount of magnetite (Fe3O4) and some sparse hematite (Fe2O3) exist on the surface of hot rolled strip when the coiling temperature reduces from 570 to 550 degrees C. The coiling temperature substantially affects the internal microstructure and magnetite phase.
Please use this identifier to cite or link to this item: