Controlling red upconversion luminescence in Gd<inf>2</inf>O<inf>3</inf>:Yb<sup>3+</sup>-Er<sup>3+</sup>nanoparticles by changing the different atmosphere

Publication Type:
Journal Article
Citation:
RSC Advances, 2016, 6 (103), pp. 101707 - 101713
Issue Date:
2016-01-01
Metrics:
Full metadata record
Files in This Item:
Filename Description Size
c6ra22754f (1).pdfPublished Version969.49 kB
Adobe PDF
© The Royal Society of Chemistry 2016. Lanthanide (Ln3+)-doped nanoparticles that produce strong red upconversion (UC) luminescence are desirable for biological applications. For nanoparticles, modification of their electronic properties and stabilization of their crystallographic phase are crucial for tuning their luminescence behaviors. Here, Yb3+-Er3+doped Gd2O3nanoparticles have been synthesized by calcining Gd2O2S in nitrogen (O2-free) and ambient air (∼21% O2), respectively. Various approaches including X-ray diffraction (XRD), transmission electron microscopy (TEM), Raman spectroscopy and thermo-gravimetric and differential thermal analyses (TG-DTA) were used to characterize the structure, morphology and phase formation mechanism of the nanoparticles. Upconversion luminescence properties were investigated by emission intensity vs. excitation power (double logarithmic relationship) and temperature dependent emission spectroscopy. The different splitting transition probabilities of the cubic and/or monoclinic phase, the probability of multiphonon relaxations and cross relaxations between Er3+ions are responsible for the efficient red emission in the cubic Gd2O3nanoparticles. More importantly, the lower phonon energy of the pure cubic sample has good thermal stability in the current detectable range of 20-100 °C. These results imply that the cubic Gd2O3upconversion nanoparticles may have multiplexing functionality in bio-imaging.
Please use this identifier to cite or link to this item: