Revised phase diagram for the Pt-Ti system from 30 to 60 at.% platinum

Publication Type:
Journal Article
Citation:
Journal of Alloys and Compounds, 2004, 375 (1-2), pp. 120 - 127
Issue Date:
2004-07-28
Metrics:
Full metadata record
Files in This Item:
Filename Description Size
Thumbnail2004000925.pdf693.61 kB
Adobe PDF
Alloys of the Ti-Pt system between 30 and 61 at.% Pt were studied using metallography with optical and scanning electron microscopy (SEM), X-ray diffraction (XRD), and differential thermal analysis (DTA). A phase of nominal composition Ti4Pt3, in the range 41.7-43.4 at.% Pt was found in samples containing between 30 and 47 at.% Pt, and was apparently formed by a peritectoid reaction between β-TiPt and Ti3Pt at 1205±10°C. The eutectic reaction between Ti3Pt and β-TiPt was found to be at ∼35 at.% Pt and 1424±10°C, and the Ti3Pt phase melted at circa 1500°C. The other phase boundaries agreed with the published literature, except that a slightly wider range was found at 1200°C for β-TiPt. © 2004 Elsevier B.V. All rights reserved.
Please use this identifier to cite or link to this item: